廠家(產(chǎn)地) | 日本出光 | 牌號 | IR2500 |
用途級別 | 注塑級 |
規(guī)格級別: | 注塑級 | 外觀顏色: | --- |
用途概述: | --- | ||
備注說明: | 特性:中粘度 |
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
基本性能 | 吸水率 | 23℃水中24h | ASTM D-570 | 0.23 | % |
熔體流動速率 | 300℃ 1.2kg | ISO 1133 ASTM D-1238 | 8 | g/10分 | |
物理性能 | 光線透過率 | 3mm厚 | ASTM D-1003 | 85-89 | % |
比重 | --- | ASTM D-792 | 1.2 | --- | |
泰伯磨耗量 | 1,000round | ASTM D-1044 | 12 | mg | |
成形收縮率 | --- | ASTM D-955 | 0.5-0.7 | % | |
機(jī)械性能 | IZOD沖擊強(qiáng)度 | 4mm with notch 3.2mm with notch | ISO 180 (ASTM D-256) | 80(100) | KJ/m2(kg?cm/cm2) |
洛氏硬度 | --- | ISO 2039-2 (ASTM D-785) | R120(M75) | --- | |
引張降伏強(qiáng)度 | --- | ISO R-527(ASTM D-638) | 64(650) | MPa(Kg/cm2) | |
引張破壞強(qiáng)度 | --- | ISO R-527(ASTM D-638) | 78(700) | MPa(Kg/cm2) | |
引張彈性率 | --- | ISO R-527(ASTM D-638) | 2300(23500) | MPa(Kg/cm2) | |
引張破壞伸率 | --- | ISO R-527(ASTM D-638) | 130 | % | |
電氣性能 | 絕緣破壞電壓 | 1.6mm厚 | ASTM D-149 | 30 | Kv/mm |
體積固有抵抗 | --- | ASTM D-257 | 1016< | Ω?cm | |
誘電率 | --- | ASTM D-150 | 2.91(2.85) | 60Hz(106Hz) | |
誘電正接 | 60Hz(106Hz) | ASTM D-150 | 6.6×10-4(9.2×10-3) | --- | |
耐電弧性 | --- | ASTM D-495 | 110 | Sec | |
熱 性 能 | 燃燒性 | 1.47mm厚 | UL 94 | V-2 | --- |
撓曲強(qiáng)度 | --- | ISO 178(ASTM D-790) | 95(970) | MPa(Kg/cm2) | |
撓曲彈性率 | --- | ISO 178(ASTM D-790) | 2350(24000) | MPa(Kg/cm2) | |
熱變形溫度 | 1.8Mpa 18.6kg/cm2 | ISO 75 (ASTM D-648) | 135 | ℃ | |
維卡軟化點(diǎn) | --- | ISO 306 | 150 | ℃ | |
線膨脹系數(shù) | --- | ASTM D-696(ASTM D-695) | 6.5 | ×10-5cm/cm/℃ |